PENGARUH PENAMBAHAN ABU TERBANG (FLY ASH) TERHADAP KUAT TEKAN MORTAR SEMEN TIPE PCC SERTA ANALISIS AIR LAUT YANG DIGUNAKAN UNTUK PERENDAMAN

REFNITA, GIFYUL (2014) PENGARUH PENAMBAHAN ABU TERBANG (FLY ASH) TERHADAP KUAT TEKAN MORTAR SEMEN TIPE PCC SERTA ANALISIS AIR LAUT YANG DIGUNAKAN UNTUK PERENDAMAN. Other thesis, Universitas Andalas.

Preview

PDF Download (41Kb) | Preview

Abstract

Gifyul Refnita Sarjana Sains di bidang Kimia Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Andalas Dibimbing oleh: Zamzibar Zuki, MP dan Yulizar Yusuf, MS Penelitan tentang pengaruh penambahan abu terbang (fly ash) terhadap kuat tekan mortar semen tipe PCC serta analisis air laut yang digunakan untuk perendaman telah dilakukan. Penelitian ini bertujuan untuk melihat pengaruh penambahan abu terbang (fly ash) terhadap mutu mortar semen tipe PCC dengan mengukur kuat tekan dan menganalisis air laut yang digunakan untuk perendaman dengan menggunakan beberapa parameter. Pengamatan dilakukan terhadap pH, TSS, TDS, kesadahan total, dan logam Kalsium pada larutan perendaman mortar. Penambahan fly ash dibuat dengan memvariasikan persentasenya yaitu 0%, 2%, 4%, dan 6% dari berat total semen tipe PCC yang digunakan. Campuran mortar tersebut kemudian di rendam pada air laut dan akuades sebagai pembanding, yang masing-masingnya selama 3, 7 dan 28 hari. Dari hasil penelitian diperoleh kuat tekan mortar semakin meningkat dengan semakin lamanya waktu perendaman, dan nilai kuat tekan mortar dengan persentase penambahan fly ash 2, 4, dan 6% pada umur 28 hari dalam perendaman air laut berturut-turut 284, 276, dan 273 kg/cm2 sedangkan dalam akuades 323, 315, dan 298 kg/cm2. Nilai kuat tekan mortar dengan persentase penambahan fly ash 2% yang direndam dalam air laut masih memenuhi SNI 15-7064-2004 yaitu 280 kg/cm2, sedangkan persentase 4 dan 6% tidak memenuhi SNI. Penurunan kuat tekan tersebut sebanding dengan kenaikan pH, kadar TSS, TDS, kesadahan total, dan kesadahan Kalsium pada larutan perendaman mortar. Kata kunci: PCC, fly ash, mortar, kuat tekan, TSS, TDS ABSTRACT INFLUENCED OF ADDING OF FLY ASH TO COMPRESSIVE STRENGTH OF MORTAR PCC AND ANALYSIS OF SEA WATER USED FOR IMMERSION By: Gifyul Refnita Bachelor of Sciences Chemistry Faculty of Mathematic and Natural Science Andalas University Advised by: Zamzibar Zuki, MP and Yulizar Yusuf, MS Research about of influenced of the adding of fly ash to compressive strength of mortar PCC and analysis of sea water used for immersing was done. This study aims to look at the influenced of adding fly ash (abu terbang) on the quality of mortar PCC by measuring the compressive strength and analyze the sea water used for immersing by using multiple parameters. Data were collected for pH, TSS, TDS, total hardness and calcium metal in solution immersion mortar. The adding of fly ash created by varying the percentage is 0%, 2%, 4%, and 6% of the total weight of the PCC used. Mortar mixture is then immersing in sea water and aquadest as controls, each with over 3, 7 and 28 days. The result showed mortar compressive strength increases with increasing duration of immersion time, and the value of compressive strength of mortar with the adding of fly ash percentage of 2, 4, and 6% at 28 days in sea water immersion respectively 284, 276, and 273 kg/cm2 whereas in aquadest 323, 315, and 298 kg/cm2. Value of compressive strength of mortar with the adding of fly ash percentage of 2% which is immersed in sea water still meets SNI 15-7064-2004 namely 280 kg/cm2, while the percentage of 4 and 6% did not meet standards. Decrease in compressive strength is proportional to the increase in pH, levels of TSS, TDS, total hardness and calcium hardness in solution immersion mortar. Keywords: PCC, fly ash, mortar, compressive strength, TSS, TDS  

Actions (login required)

View Item