SINTESIS DAN KARAKTERISASI BLENDING ZnO-Mn(II) ASETONITRILKLORIDA DAN UJI PENDAHULUAN AKTIFITAS KATALITIKNYA PADA REAKSI TRANSESTERIFIKASI

HIDAYATURRAHMAT, HIDAYATURRAHMAT (2014) SINTESIS DAN KARAKTERISASI BLENDING ZnO-Mn(II) ASETONITRILKLORIDA DAN UJI PENDAHULUAN AKTIFITAS KATALITIKNYA PADA REAKSI TRANSESTERIFIKASI. Other thesis, ANDALAS UNIVERSITY.

Preview	PDF Download (19Kb) | Preview
Preview	PDF Download (135Kb) | Preview
Preview	PDF Download (14Kb) | Preview

Abstract

vi INTISARI SINTESIS DAN KARAKTERISASI BLENDING ZnO-Mn(II) ASETONITRILKLORIDA DAN UJI PENDAHULUAN AKTIVITAS KATALITIKNYA PADA REAKSI TRANSESTERIFIKASI Hidayaturrahmat (0910412047) Dibimbing oleh Dr.Syukri dan Emdeniz, MS Sintesis dan karakterisasi blending garam MnCl2 dengan ZnO serta uji pendahuluan aktivitas katalitiknya pada reaksi transesterifikasi telah dilakukan. Garam MnCl2 dengan berbagai variasi molar dilarutkan dalam asetonitril membentuk kompleks Mn(II)asetonitril. Kompleks tersebut kemudian diblending dengan ZnO membentuk Mn(II)asetonitril-ZnO. Hasil karakterisasi dengan FT-IR menunjukan adanya vibrasi C-N asetonitril yang mengalami shifting yang menunjukan adanya interaksi antara kompleks dan ZnO. Uji stabilitas katalis ini dilakukan dengan melakukan stirring antara katalis dengan asetonitril selama 24 jam. Nilai metal leaching dari katalis ini relatif kecil (< 0,1 % ) menunjukan logam Mn pada katalis ini cukup stabil. Uji pendahuluan aktivitas katalitik dari katalis ini pada reaksi tarnsesterifikasi menunjukkan hasil yang siginifikan dengan persentase puncak area metil ester berdasarkan GCMS sebesar 85,99 %. Kata kunci : katalis kompleks, blending katalis, seng oksida, transesterifikasi vii ABSTRACT SYNTHESIS AND CHARACTERIZATION OF BLENDING ZnO – Mn(II)acetonitrilechloride AND PRELIMINARY TEST OF ITS CATALYTIC ACTIVITY IN TRANSESTERIFICATION REACTION Hidayaturrahmat (0910412047) Adviced by Dr.Syukri and Emdeniz, MS Synthesis and characterization of ZnO which blended with MnCl2 salt and preliminary test of its catalytic activity in the transesterification reaction has been carried out . MnCl2 salt with various molar dissolved in acetonitrile to form complexes of Mn ( II ) acetonitrile . The complex was blended with ZnO to form Mn ( II ) acetonitrile - ZnO . The characterization of the compound by Fourier transform Infra Red (FT – IR) showed the presence of CN vibrations in acetonitrile lead to the shifting that shows the interaction between the complex and ZnO . Catalyst stability test was carried out by stirring the catalyst with acetonitrile for 24 h . Leaching value of the catalyst metal is relatively small ( < 0.1 % ) showed Mn metal in the catalyst is quite stable . Preliminary test in the catalytic activity of this catalyst through the transesterification reaction showed significant results with the 85.99 % of methyl ester peak area from Gas Chromatography Mass Spectrometry (GC-MS). Keywords : blending of catalyst , metal complexes, zinc oxide , transesterification

Actions (login required)

View Item